34CrNiMo6 / 1.6582 Steel
34CrNiMo6 steel is a common nickel-molybdenum alloy steel accding to DIN standard,and 1.6582 steel is under W-Nr Germany standard.It is a high strength steel and has good comprehensive mechanical properties.DIN 1.6582 steel is widely used in the manufacture of the camshaft and connecting rod of engine parts, poor processability, belongs to the typical difficult-to-machine materials.
Carbon:0.30/0.38; Silicon:Max0.40; Manganese:0.50/0.80;
Chromium:1.30/1.70; Molybdenum:0.15/0.30; Nickel:1.30/1.70;
AISI/ASTM: 4340; JIS/KS: SNCM439;
EN 10277 – 5 : 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering
EN 10083 – 3 : 2006 Steels for quenching and tempering. Technical delivery conditions for alloy steels
EN 10269 : 1999 Steels and nickel alloys for fasteners with specified elevated
EN 10263 – 4 : 2001 Steel rod, bars and wire for cold heading and cold extrusion.
EN 10250 – 3 : 2000 Open steel die forgings for general engineering purposes.
4.Form & Size
-DIN 34CrNiMo6 Alloy Steel as Forged
1)Fuhongsteel manufactures and supplies 34CrNiMo6 forged steel round bars,square bar,flat bar,shaft,and blocks.
2)DIN 34CrNiMo6 alloy steel size available:
(Forged flat bars,Blocks,Shafts and forging pieces can be customized)
-W-Nr 1.6582 Alloy Steel as Rolled
1)Fuhongsteel is a quality steel supplier of 1.6582 rolled steel round bars.
2)W-Nr 1.6582 alloy steel round bar size available:
Length: 3,000-10,000mm(can be customized)
5.Tolerances on Dimension & Straightness
3)Deviation from straightness:with 360° rotary device 2mm/meter(max)
1)Chemical composition:Related DIN 7527-6 , EN 10250-3
2)Mechanical properties -Tensile strength -Yield point -Percentage reduction of area after fracture -Elongation after fracture -Impact test: Impact test must be done on three (3) different ISO-V samples at +20 C°
3)Non metallic inclusions
4)Grain size:According to DIN 50601 more than 5,preferred to 8;
5)Ultra sonic testing 360° complete round testing: Ultra sonic according to EN 10228-3
34CrNiMo6 steel is often used in the manufacture of shaft under high load, such as connecting rod structure.DIN 1.6582 steel is also made the surface is hard wear-resisting and heart of flexible components, such as gear.It is also widely used in engine camshaft and connecting rod parts.
1)Preheat 1.6582 forged alloy steel carefully.
2)Raise the forging temperature up to 1150-1200°C.
3)Keep the forging temperature above 850°C.
Hardening&Tempering(quenched and tempered and after stress relieved)
1)Heating 34CrNiMo6 steel uniformly to 850°C;
2)W-Nr 1.6582 alloy steel should be quenched in the oil;
3)Heat the material to the temperature 550°C;
4)Soak at this temperature for at least 2 hours;
5)1.6582 alloy steel should be cooled in the furnace.
In case after QT a straightening process is necessary then the products should be tempered and distorsion-poor annealed with at least more than 625°C.
1)Heating 1.6582 forged steel thoroughly to 800-850°C;
2)Cool slowly to the temperature 550°;
3)Complete annealing the steel in the air.
1)heat DIN 1.6582 steel until the temperature up to 850°C;
2)Then cool W-Nr 34CrNiMo6 steel down to the room temperature in the air.
Enquiry for DIN 34CrNiMo6 / 1.6582 steel round bars,square/flat bars,rollers,shafts and blocks.